Paste-type resins

SPECIAL RESINS FOR AUTO PUTTY AND METAL SURFACE PUTTY

Polres UPE and Polres GMP are DCPD-based amine-containing orthophthalic resins specially developed for auto putty and metal surface putties. They offer high filler acceptance, superior adhesion strength and excellent flexibility.

GET TECHNICAL CONSULTING

TECHNICAL SPECIFICATIONS

Up to 80% high fill acceptance
Superior metal surface adhesion
Controlled flexibility and crack resistance
Excellent sanding performance

Polres UPE

DCPD Based Orthophthalic Resin

Resin with high filling capacity and excellent adhesion strength, developed for car putty and general metal surface putties.

High fill acceptance (up to 80%)
Excellent metal adhesion
Controlled flexibility
Cracking resistance

Polres GMP

Improved Flexibility Resin

Resin designed for galvanized surfaces and special applications requiring flexibility, offering superior flexibility and adhesion performance.

Superior flexibility
Galvanized surface compatibility
Thermal expansion compliance
Anti-cracking

Technical Advantages

High Fill Acceptance

Possibility of economical paste production with filling rates up to 80%

Superior Adhesion

Excellent adhesion on metal, galvanized and various surfaces

Cracking Resistance

Perfect surface without cracking and shrinkage during drying

Application Areas

Auto Putties

Metal Surface Putties

Galvanized Surfaces

Filled Repair Putties

Surface Correction

Filling After Welding

Notch Fillers

Industrial Repair

Performance Specifications

Excellent Sanding Performance

Putties made from both resins have excellent sandability and drying of the metal surface as a result of shrinkage. The putty surface can be sanded smoothly, dust formation is minimal and no scratches are formed on the surface. It provides excellent surface smoothness after drying.

Flexibility and Cracking Resistance

The flexibility of the resins prevents the car putty from cracking due to drying on the surface. Especially Polres GMP prevents crack formation by adapting to thermal expansion and contraction on galvanized surfaces. In this way, long-lasting and durable putty applications are possible.

Polres Polyester Product Comparison

0 products selected

Features	Polres UPE	Polres GMP
Description	Putty Type	Putty Type
Chemical Content	Orthophthalic / Standard Glycol / DCPD	Orthophthalic / Standard Glycol / DCPD
Accelerator	Optional	Optional
Reactivity	Medium	Medium
Thixotropy	Optional	Optional
Viscosity (cps)	500-550	500-550
Gel time (min.)	12-14	10-16
Monomer ratio (%)	34-38	34-38
HDT (°C)	55-65	50-60
Barkol hardness 934-1	30-40	30-40
Flexural strength (MPa)	50-70	65-75
Tensile strength (MPa)	15-30	10-30
Impact resistance (kJ/m²)	7-12	7-12
Features	High filler acceptance Easy sanding Excellent making and strength Enhanced flexibility Polres can mix with GMP	High filler acceptance Easy sanding Excellent making and strength Enhanced flexibility Polres can be mixed with UPE
TDS/SDS	TDS or SDS Request	TDS or SDS Request

Modification Codes

T Thixotropic	WV Winter Version	UV UV stabilized
A Cobalt accelerator	SW Summer Version	TT Spray Application
B Blue indicator	HV High Viscosity	FT Brush/Roller Application
D Filled	LV Low Viscosity	Color: White
ABP Amin accelerator	FR Non-flammable	Color PRO color
TE Terephthalic acid	FRHI Halogenated Isophthalic Flame Retardant	Color Light color
LSE Low styrene emission	FRH Halogenated Flame Retardant	Color: Transparent
H Halogenated	M Acrylic Modified